JLT-602 Single Sided Mono Filament Tape

Item NO.: JLT-602

Backing: PET

Adhesive: Synthetic Rubber

Reinforcement: Fiberglass

Elongation: 3-5%

JLT-602 is a reinforced unidirectional filament tape based on PET film and fiberglass. It is an economical type, suitable for all medium-strength packaging, bundling, and reinforcement applications during transportation, such as carton sealing, tear strips for courier bags, and pipe wrapping.

✔ Economical Choice
✔ Medium-Strength Reinforcement
✔ PET & Fiberglass Base
✔ Unidirectional Tensile Strength
✔ Versatile Packaging Applications
✔ Enhances Transit Security

Safety Data Sheet Technical Data Sheet

Why Choose JL3® Brand Filament Tape?

Core Advantages of JL3® FILAMENT Tape

Combining quality and price
Backed by over a decade of iterative optimization, JL3® delivers quality on par with leading international brands while maintaining strict cost efficiency.
Integrated Solutions
As an integrated enterprise combining manufacturing, R&D, and trading, our dedicated sales team provides precise, customized solutions tailored to your specific packaging requirements.
Rigorous QC
Every shipment undergoes strict quality inspection prior to dispatch to ensure reliable batch consistency and performance stability.
Rapid after-sales response
Standardized after-sales protocol: issues logged within 2 hours, technical response within 24 hours, and definitive resolution within 48 hours.

JLT-602 Reinforced Filament Tape

Product Features

Filament Detail

Application Scenario

Physical Properties	Standard	Metric	Test Method
Reinforcement	Fiberglass
Adhesive	Synthetic Rubber
Backing	PET
Color	Clear
Total Thickness	3.9 mils	0.10 mm	ASTM D-3652 / GB/T7125
Peel Adhesion 90°	83 oz/in	23N/25 mm	ASTM D-3330 / GB/T2792
Holding Power	36±5 h	36±5 h	ASTM D-3654 / GB/T4851
Tensile strength	124 lbs/in	550N/25 mm	ASTM D-3759 / GB/T7753
Elongation at Break	3-5%	3-5%	ASTM D-3759 / GB/T7753
Service Tem.--Mini	23℉	-5℃	BC/BD-220SE
Service Tem.--Max	158℉	70℃	DHG-9055A

Note: All specifications are tested under controlled temperature and humidity conditions (23±2°C, 50±5% RH). Results may vary based on application. Request a free sample to validate performance in your environment.